Large area, uniformly low dislocation density GaN substrate and process for making the same

ABSTRACT

Large area single crystal III-V nitride material having an area of at least 2 cm 2 , having a uniformly low dislocation density not exceeding 3×10 6  dislocations per cm 2  of growth surface area, and including a plurality of distinct regions having elevated impurity concentration, wherein each distinct region has at least one dimension greater than 50 microns, is disclosed. Such material can be formed on a substrate by a process including (i) a first phase of growing the III-V nitride material on the substrate under pitted growth conditions, e.g., forming pits over at least 50% of the growth surface of the III-V nitride material, wherein the pit density on the growth surface is at least 10 2  pits/cm 2  of the growth surface, and (ii) a second phase of growing the III-V nitride material under pit-filling conditions.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No.11/856,222 filed on Sep. 17, 2007, now U.S. Pat. No. 7,879,147 issued onFeb. 1, 2011, which is in turn a divisional of U.S. patent applicationSer. No. 10/712,351 filed on Nov. 13, 2003, now U.S. Pat. No. 7,323,256issued on Jan. 29, 2008. The disclosures of the foregoing U.S. patentapplications and patents are hereby incorporated herein by reference intheir entireties, for all purposes.

GOVERNMENT RIGHTS IN INVENTION

The invention was made in the performance of U.S. Navy Contract NumberN0001402C0321. The U.S. Government has certain rights in the invention.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to large area, uniformly low dislocationdensity gallium nitride material, such as is useful in the manufactureof microelectronic and opto-electronic devices, such as light emittingdiodes, laser diodes, opto-electronic sensors, opto-electronic switches,high electron mobility transistors, etc., as well as a method for makingsuch gallium nitride material.

2. Description of the Related Art

Gallium nitride (GaN) and related III-V nitride alloys have applicationsin light emitting diodes (LED) and laser diodes (LD) and in electronicdevices. The performance of the GaN-based device strongly depends on thecrystal defects of the device layer, especially the density of threadingdislocations. For blue and UV laser diodes, a dislocation density ofless than 3×10⁶ cm⁻² is preferred for longer lifetime. Furthermore, GaNdevices grown on native gallium nitride substrates are preferred forimproved device performance and simplified design and fabrication.

Gallium nitride substrates can be prepared by various methods. Porowskiet al. U.S. Pat. No. 5,637,531 discloses a method of growing bulk GaN athigh nitrogen pressure. Metallic gallium is reacted with gaseousnitrogen to form gallium nitride crystals at the surface of the galliummelt. A temperature gradient is provided in the reactor vessel,resulting in supersaturation of nitrogen atoms in the cooler region ofthe reactor, and growth of gallium nitride crystals. The growth pressurein the Porowski et al. process is about 10 kbar and growth temperatureis about 1400° C. The dislocation density of material produced by thePorowski et al. process is as low as 100 cm⁻², however, the maximum sizeof the GaN produced by this method has been limited to about 10 mmplatelets (S. Porowski and I. Grzegory, J. Cryst. Growth, Vol 178, 174(1997), M. Bockowski, J. Cryst. Growth, Vol 246, 194 (2002)).

Hydride vapor phase epitaxy (HVPE) has been utilized to produce galliumnitride substrates. Tischler et al. discloses in U.S. Pat. No. 5,679,152a method of producing single crystal GaN substrates by first growing athick GaN film on a compatible sacrificial substrate and then etchablyremoving the sacrificial base substrate at a temperature near the growthtemperature to produce the freestanding GaN substrate. Another method ofseparating the grown gallium nitride film from the substrate is tooptically induce decomposition at the interface between the grown filmand the substrate. Kelly et al. discloses in U.S. Pat. No. 6,559,075 amethod for separating two material layers by using laser energy todecompose the interface layer. For GaN grown on sapphire substrates, alaser with energy larger than the bandgap of GaN, but smaller than thebandgap of sapphire, is used. When the laser shines through the sapphiresubstrate, the laser energy is absorbed at the GaN-sapphire interface.With sufficient laser energy density, the GaN in the interface region isdecomposed into metallic gallium and gaseous nitrogen, therebyseparating the GaN film from the sapphire substrate. A freestanding GaNwafer almost 2″ in diameter was produced using this method (see, forexample, M. K. Kelly et al., Jpn. J. Appl. Phys. Vol. 38, pp. L217-L219,1999). Motoki et al. discloses in U.S. Pat. No. 6,413,627 a method ofmaking a single crystal GaN substrate material, by first growing a thickGaN film on a gallium arsenide substrate and then eliminating thesubstrate. The dislocation density for the typical HVPE gallium nitrideis about 1×10⁷ cm⁻².

Motoki et al. in U.S. Pat. No. 6,468,347 and U.S. Published PatentApplications 2003/0080345 and 2003/0145783 describe methods to producegallium nitride single crystal substrates with low dislocation densityin certain areas but high dislocations in other areas. The highdislocation density areas are disclosed as being randomly distributed,or distributed in a predetermined pattern, e.g., in the form of periodicstripes, with the low dislocation density regions dispersed between thehigh dislocation density areas. In U.S. Pat. No. 6,468,347, Motoki etal. thought the GaN material produced had low dislocation density, butin U.S. Published Patent Applications 2003/0080345 and 2003/0145783,Motoki et al. clarified that material produced by the process disclosedin U.S. Pat. No. 6,468,347 had high dislocation density area randomlydispersed in the low dislocation density area. In U.S. Published PatentApplication 2003/0080345, Motoki et al. disclosed methods to place thehigh dislocation density areas in a predetermined pattern as periodicdots. In U.S. Published Patent Application 2003/0145783, Motoki et al.disclosed methods to place the high dislocation density area in the formof periodic stripes.

The presence of high dislocation density areas on the GaN substratenecessitates precise alignment of the device structure on the low defectareas. Furthermore, the non-uniform distribution of defects mayadversely affect the growth of the device layer on the GaN substrate.

Vaudo et al. U.S. Pat. No. 6,440,823 teaches the use of pitted growth tocollect and annihilate dislocations, as well as high surface morphologyconditions to subsequently close the pits.

Since the performance of the GaN-based laser diodes and other devices iscritically dependent on the nature and extent of crystal defects in thedevice layer, which in turn depends on the defect structure andmorphology of the GaN substrate, there is a compelling need foruniformly low dislocation density GaN substrates. Furthermore, low-costmanufacturing of GaN-based devices requires large area substrates. Theprior art has failed to provide uniformly low dislocation density, largearea GaN substrates.

SUMMARY OF THE INVENTION

The present invention relates to large area, uniformly low dislocationdensity gallium nitride, and process for making same.

In one aspect, the invention relates to large area single crystal III-Vnitride material with uniformly low dislocation density on at least onesurface thereof.

In another aspect, the invention relates to large area, uniformly lowdislocation density single crystal gallium nitride, having a large areaof greater than 15 cm², a thickness of at least 0.1 mm, an averagedislocation density not exceeding 1×10⁶ cm⁻², and a dislocation densitystandard deviation ratio of less than 25%.

Another aspect of the invention relates to an article, including largearea single crystal III-V nitride material with uniformly lowdislocation density on at least one surface thereof.

A further aspect of the invention relates to a wafer including largearea single crystal gallium nitride material with uniformly lowdislocation density on at least one surface thereof.

In another aspect, the invention relates to an electronic devicearticle, including a wafer comprising large area single crystal galliumnitride material with uniformly low dislocation density on at least onesurface thereof, and an electronic device structure fabricated on suchwafer.

Additional aspects of the invention relate to large area single crystalIII-V nitride material, e.g., GaN, with uniformly low dislocationdensity on at least one surface thereof, as grown under single crystalIII-V nitride growth conditions slightly deviated from optimal singlecrystal III-V nitride growth conditions, as well as to wafers formed ofsuch material.

Yet another aspect of the invention relates to a vapor phase growthprocess for forming a large area, uniformly low dislocation densitysingle crystal III-V nitride material on a substrate, such processincluding (i) a first phase including one or more steps of growing theIII-V nitride material on the substrate by a vapor phase growthtechnique under pitted growth conditions, and (ii) a second phaseincluding one or more steps of growing the III-V nitride material by thevapor phase growth technique under pit-filling conditions effectingclosure of pits and annihilation of defects on a growth surface of theIII-V nitride material.

A further aspect of the invention relates to a vapor phase growthprocess for forming a large area, uniformly low dislocation densitysingle crystal III-V nitride material on a substrate, such processincluding (i) a first phase of growing the III-V nitride material on thesubstrate by a vapor phase growth technique under pitted growthconditions forming pits over at least 50% of the growth surface of theIII-V nitride material wherein the pit density on the growth surface isat least 100/cm² of the growth surface at the end of the first phase,and (ii) a second phase of growing the III-V nitride material underpit-filling conditions that fill the pits to produce an essentiallypit-free surface.

Other aspects, features and embodiments of the invention will be morefully apparent from the ensuing disclosure and appended claims. dr

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a differential interference contrast (DIC) optical micrographof a textured surface morphology of HVPE GaN film grown on a sapphiresubstrate under optimized growth conditions including a growthtemperature of 1030° C., an NH₃/HCl ratio of 30, a growth time of 1hour, and a growth rate of 116 microns/hour.

FIG. 2 is a DIC optical micrograph of a pitted surface morphology ofHVPE GaN film grown under conditions of slightly higher NH₃ flow thanthe optimal condition, wherein the growth temperature was 1030° C., theNH₃/HCl was 58, the growth time was 1 hour, and the growth rate was 268microns/hour.

FIG. 3 is a DIC optical image of a GaN surface after mechanical polishand chemical mechanical polish (CMP) finish, wherein the as-grown waferblank prior to such polishing and CMP exhibited a pit-free texturedsurface, similar to the one shown in FIG. 1.

FIG. 4 is a DIC optical micrograph of a GaN surface after mechanicalpolish and CMP finish, wherein the as-grown wafer blank prior to suchpolishing and CMP exhibited a high density of pits on the surface,similar to the surface shown in FIG. 2, and the pits were removed duringpolish.

FIG. 5 is a room-temperature total-intensity catholuminescence image ofa GaN surface having a morphology similar to that of the FIG. 4 GaNwafer, wherein the dark spots correspond to crystalline defects. Thesurface was polished mechanically and finished with a CMP process.

FIG. 6 is an atomic force microscope (AFM) image (50 microns×50 microns)of a CMP-finished GaN that had surface morphology similar to the waferwhose surface is shown in FIG. 4. The GaN material was grown withconditions that favor pit formation (pitted process) and growth pitswere removed during polish. The distribution of the etch pits anddislocation density was not uniform and was concentrated near the centerof the recessed area.

FIG. 7 is an atomic force microscope image (50 microns×50 microns) of aCMP-finished GaN that had surface morphology similar to the wafer whosesurface is shown in FIG. 3. The GaN material was grown with a pit-freeprocess. The distribution of the etch pits and dislocation density isuniform.

FIG. 8 is a DIC optical image of a GaN surface after CMP and etchingwith hot phosphoric acid. The GaN was grown under pitted growthconditions to a thickness of 5 mm. After CMP and hot phosphoric acidetching, the dislocations are decorated as etching pits. Thedistribution of the pits is not uniform.

FIGS. 9A-9E are a series of schematic illustrations showing the growthof a GaN substrate article according to one embodiment of the presentinvention, including provision of a substrate (FIG. 9A), growth of GaNunder pitted growth conditions producing smaller pits in the GaN film onthe substrate, with lines perpendicular to growth surface representingthreading dislocations (FIG. 9B), continued growth wherein the pits growlarger, concentrating the dislocations under the pitted growthconditions (FIG. 9C), growth of GaN under pit-filling conditions,wherein pits grow smaller under the pit-filling growth conditions,partially annihilating the dislocations, until pits are completelyfilled and all dislocations meet at the moment of pit closure, leaving afew dislocations remaining (FIG. 9D), and further growth of defect-freeGaN to produce the product uniformly low dislocation density large areaGaN material (FIG. 9E).

FIGS. 10A-10B are DIC optical microscope images (FIG. 10A, focusing onthe wafer surface; FIG. 10B, focusing under the surface of the same areaas FIG. 10A) of the dislocation distribution of a GaN wafer according tothe present invention. The dislocations were decorated as etch pits bychemical mechanical polish and hot phosphoric acid etching. The image inFIG. 10A shows the top surface and the image in FIG. 10B is focusedunder the surface with different contrast to highlight the differencesof the material under the surface. The circles indicate pit-fillinggrowth underneath the surface. The width of each image was 250 μm.

FIG. 11 is a photograph of a 2.3 inch diameter double side polishedgallium nitride wafer produced according to one embodiment of thepresent invention.

FIG. 12 is a differential interference contrast optical microscope imageof the dislocations on a GaN wafer according to one embodiment of thepresent invention. Dislocations were decorated by chemical mechanicalpolishing and hot phosphoric acid etching.

FIG. 13 is a 100×100 μm AFM scan of a GaN wafer according to oneembodiment of the present invention. Dislocations were decorated bychemical mechanical polishing and hot phosphoric acid etching.

DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS THEREOF

The present invention relates to uniformly low dislocation density andlarge-area gallium nitride substrates and methods of making the same.

As used herein, the term “large area” in reference to the galliumnitride substrate article of the present invention, means that sucharticle has a surface area of at least 2 cm². In preferred practice, thelarge area gallium nitride substrate article of the present inventionhas a surface area for GaN epitaxial growth thereon, that is greaterthan 15 cm². The thickness of such large area, low dislocation densityGaN material may be any suitable thickness, and preferably is at least0.1 millimeter (mm).

As used herein, the term “low dislocation density material” refers toGaN or other III-V nitride material having a dislocation density notexceeding 3×10⁶/cm² of growth surface area. In preferred practice of theinvention, the dislocation density of the uniformly low dislocationdensity large area material does not exceed about 1×10⁶/cm², and mostpreferably such dislocation density does not exceed 1×10⁵dislocations/cm² on the large area growth surface of the substrate.

As used herein, the term “uniformly low dislocation density” inreference to the gallium nitride or other III-V nitride single crystal,low dislocation density material of the invention, means that suchmaterial on its large area growth surface has dislocations distributedrandomly and uniformly on such large area surface.

For example, in randomly selected measurement areas (50 μm×50 μm, forinstance), the density of the dislocations and the distribution of thedislocations in the randomly selected areas are similar to one another.It will be appreciated that the total area measured on the large areasurface must be sufficiently large so that the dislocation density ismeasured in a statistically significant manner, and the randomlyselected measurement areas within such total area must be small enoughto exhibit sensitivity to small-scale periodic variation. If manydislocation density measurements are statistically sampled in randomlyselected locations over large areas, the average of the measurements andstandard deviation of the measurements are obtained.

The average of the dislocation density measurements determined in thismanner for the GaN or other III-V nitride single crystal material of theinvention on its large area growth surface, hereafter referred to asaverage dislocation density (ADD), does not exceed 3×10⁶ cm⁻² and thedislocation density standard deviation ratio, hereafter referred to asDDSDR, determined as (standard deviation of the dislocation density ofrandomly selected locations over the large area)/(average dislocationdensity), preferably is less than 50%. In various specific embodimentsof the invention, the ADD more preferably is below 1×10⁶ cm⁻² and theDDSDR more preferably is less than 25%. Still more preferably, the DDSDRis less than 10%, and most preferably the DDSDR is less than 5%.Dislocation density can be measured with a transmission electronmicroscope (TEM). Alternatively, dislocations can be decorated as etchpits by chemical mechanical polishing and/or etching in hot phosphoricacid, and the density of the etch pits can be measured with an opticalmicroscope, or a scanning electron microscope (SEM) or an atomic forcemicroscope (AFM) (Xu et al., J. Electronic Materials, Vol 31, 402, 2002,J. Crystal Growth, Vol 246, 223 (2002), and Physica Status Solidi (c),2003).

As used herein, the term “essentially pit-free surface” as applied tothe growth surface of the single crystal III-V nitride material at theconclusion of the pit-filling growth in the method of the invention,means a surface having a pit density not exceeding 3 pits/cm² of surfacearea. The term “pit,” as used herein, refers to cavities, depressions,localized indentations, and similar surface artifacts on the growthsurface. Pits frequently, but not invariably, will have crystallographicboundaries, e.g., hexagonal or dodecagonal boundaries in the case ofc-plane growth, but may also be formed with geometrically irregularboundaries or boundaries of other conformations.

The present invention achieves a uniformity of low dislocation densityon a large area gallium nitride substrate, which the prior art has beenunable to obtain. By providing a large area growth surface having a lowlevel of randomly and uniformly distributed dislocations, the presentinvention achieves a substantial advance in the art, sincemicroelectronic devices can be fabricated anywhere on such large areasurface, without concern for high defect regions such as arecharacteristic of prior art practice. In such prior art practice, theexistence of localized high defect regions severely limits the freedomand flexibility of the integrated circuitry fabrication, and anyregistration of microelectronic and/or opto-electronic device structurewith such high defect regions can render the ultimate microelectronicand/or opto-electronic device deficient or even useless for its intendedpurpose.

Large area, uniformly low dislocation density gallium nitride materialmay be formed in accordance with the present invention utilizing anysuitable growth technique, e.g., hydride vapor phase epitaxy (HVPE),metal-organic vapor phase epitaxy (MOVPE), metal-organic chloride method(MOC), sublimation, molecular-beam epitaxy (MBE), gas source MBE,metal-organic MBE, sputtering, reactive sputtering, reactivesublimation, etc. In addition, any combination of one or more techniqueseither together or in sequence may be considered a suitable growthtechnique. In general, any suitable vapor phase growth method may beemployed that effectively delivers growth species for GaN film formationto the gallium nitride growth surface.

Accordingly, while the ensuing disclosure will be directed primarily tovapor phase formation of large area, uniformly low dislocation densityGaN by HVPE, it will be appreciated that such disclosure is of anillustrative character only, and that the use of alternative film growthtechniques is contemplated in the broad practice of the presentinvention.

In the use of HVPE processing to form large area, uniformly lowdislocation density GaN in accordance with the present invention, theGaN growth rate, film morphology and material quality are selectivelyoptimizable by appropriate selection of ammonia flow rate, hydrogenchloride flow rate and growth temperature, for the specific reactorconfiguration that is employed, as is readily determinable within theskill of the art based on the disclosure herein. It will therefore berecognized that exact growth parameters for achieving the uniformly lowdislocation density, large area gallium nitride material of theinvention will vary with the specific vapor phase deposition reactorthat is employed to form the GaN material of the invention. Theoptimization of the GaN growth process may for example be carried out bya design of experiments (DOE) approach where several parameters arevaried, or by varying one of the ammonia flow rate, HCl flow rate andgrowth temperature parameters while keeping the other parametersconstant and determining the GaN growth rate, film morphology andmaterial quality that are thereby achieved for the GaN film, andrepeating such iterative change of process conditions for the second andthird parameters (of the ammonia flow rate, HCl flow rate and growthtemperature parameters) in turn, to establish an optimal set of processconditions, from which conditions can be determined that produce thedesired uniformly low dislocation density, large area GaN material insuccessive process stages of pit-forming growth and pit-filling growth,as hereinafter more fully described

The surface morphology of GaN films formed by the vapor phase HVPEprocess will strongly depend on the growth conditions, particular thegrowth temperature and NH₃:HCl ratio. Two characteristic surfacemorphologies are observed for crystalline gallium nitride films grown byHVPE. FIG. 1 shows one typical textured surface morphology of galliumnitride film grown on a sapphire substrate at optimal growth temperatureand NH₃/HCl ratio. The specific optimized growth conditions for growthof this GaN surface included a growth temperature of 1030° C., anammonia to hydrogen chloride ratio, NH₃:HCl, of 30 and a growth rate of116 μm/hr. As shown in FIG. 1, the GaN surface produced under theseoptimized GaN growth conditions exhibited hillock surface morphology.

FIG. 2 shows a pitted surface morphology of HVPE GaN film that istypical of GaN material that is grown under conditions of slightly lowertemperature, or slightly higher ammonia flow (higher NH₃:HCl ratio), orboth slightly lower temperature and slightly higher ammonia flow (higherNH₃:HCl ratio), than is employed in the optimal process conditions.Although the surface exhibits pits in this sub-optimal regime of lowertemperature and/or higher ammonia flow rate than the optimal processconditions, the GaN film exhibits single crystalline character and theextent of pitting is desirably at a high level, so that as much of thegrowth surface as possible is covered with pit formations. Thepit-forming phase of the growth process of the present invention isdesirably carried out to yield a pit density on the growth surface ofthe GaN material that is at least 100 pits/cm² of growth surface area,preferably being greater than 500 pits/cm² of growth surface area at theend of the pitted growth phase.

FIG. 2 is an optical micrograph image of a GaN surface grown under thefollowing pit-forming growth conditions: growth temperature=1030° C.,NH₃:HCl ratio=58, growth time=1 hour and growth rate=268 microns/hour.

After the growth of a self-supporting thickness of GaN on a compatiblesubstrate, the substrate can be removed to yield a freestanding GaNwafer blank. The freestanding GaN wafer blank then may be subjected topost-growth processing steps, such as lapping, polishing, and chemicalmechanical polishing (CMP) to produce the finished GaN wafer, as morefully described in Xu et al. U.S. Pat. No. 6,488,767. The surfacemorphology of the CMP-finished GaN wafer is related to the morphology ofthe wafer blank prior to processing.

FIG. 3 is a differential interference contrast (DIC) optical microscopeimage of a CMP-finished GaN wafer. The starting as-grown wafer blank hada pit-free textured surface morphology, similar to the surfacemorphology shown in FIG. 1. As shown in FIG. 3, the CMP-finished waferwas very smooth and featureless.

On the other hand, if the starting as-grown GaN wafer blank has a pittedsurface morphology, the CMP-finished wafer is not featureless. FIG. 4 isa differential interference contrast (DIC) microscope image of a pittedGaN wafer after lapping, mechanical polishing and CMP finishing. Eventhough the pits are completely removed during the mechanical polishingstep, the CMP-finished wafer surface appears to have two regions, one ofwhich is recessed slightly below the other. The shape and size of therecessed regions are very similar to the shape and size of the pits thatwere present during growth at the same cross-section. The recessedregion corresponds to the material growth in the pits, in a growthdirection along the facets of the pits and the other region correspondsto the material that is grown in a growth direction along the c-axis.

There is a subtle difference between the material grown in therespective different growth directions. The impurity concentration ishigher for the material grown along the surface of the pits than in thematerial grown along the c-axis. The rate of chemical mechanicalpolishing of the respective materials is correspondingly slightlydifferent, with the material grown with the growth direction along thefacets of the pits having a higher removal rate than the material grownalong the c-axis, leading to the observed indentation. Even themicroscopic crystal growth direction inside the pits is along the facetsof the pits, and the surface is still a c-axis surface after removingthe pits by polish and CMP. The degree of indentation can be minimizedby using a smaller grit diamond material in the mechanical polishingstep prior to the CMP step, and shorter CMP processing time.

These two surface regions (one region corresponding to the materialgrowth in the pits, in a growth direction along the facets of the pits,and the other region corresponding to the material grown in a growthdirection along the c-axis) also have slightly differentcatholuminescence (CL) properties.

FIG. 5 is a room-temperature total-intensity catholuminescence image ofa GaN surface, as polished mechanically and finished with a CMPfinishing process. FIG. 5 thus reflects a mapping of total roomtemperature catholuminescence intensity for a CMP-finished GaN waferhaving a morphology similar to the wafer whose optical micrograph isshown in FIG. 4. The surface has two regions that have differentcatholuminescent properties. The recessed area exhibited a high total CLintensity at room temperature.

The crystalline defects (dislocations) in the material shown in FIG. 5are observable in the CL mapping as dark spots corresponding todislocations. The dislocations are concentrated near the center of therecessed area. The chemical mechanical polishing process also decoratesthe threading dislocations as pits that are observable by AFM.

FIG. 6 is an AFM image of a 50 micron×50 micron area of a CMP-finishedGaN wafer having a surface similar to that shown in FIG. 4 hereof andgrown by a pitted surface growth process. The distribution of thecrystal defects was not uniform, and the center region of the recessedarea had a higher density of dislocations. The overall dislocationdensity was about 1×10⁷/cm² of GaN surface area, although many 10micron×10 micron areas of the surface have dislocation density below5×10⁶/cm². This dislocation distribution was associated with HVPE growthconditions yielding a pitted surface morphology.

When GaN growth conditions were employed that yielded pit-free texturedsurfaces like the surface shown in FIG. 1, the distribution ofdislocations was quite different. FIG. 7 is an AFM image of a 50micron×50 micron area of a CMP-finished GaN material with surfacemorphology similar to that of the GaN surface shown in FIG. 3, and grownusing a pit-free process. The distribution of the etch pits anddislocation density of the GaN surface was uniform, with an averagedislocation density of the GaN surface on the order of about 1×10⁷dislocations/cm².

Although the average dislocation density of GaN films produced byconditions that yield pitted surface morphology (i.e., films grown by apit-forming growth process) and the average dislocation density of GaNfilms produced by conditions that yielded pit-free textured surface wasapproximately the same, the distribution of the dislocations wasdifferent in the two processes. Specifically, the pit-forming growthprocess yielded films with randomly distributed low dislocation areasand high dislocation areas. The origin of this low dislocation densityarea morphology in the pit-forming growth process related to the factthat under pitted growth conditions, surface pits were formed during thegrowth of the GaN material. These pits were typically faceted pits inthe shape of inverse hexagonal pyramids and occasionally inversedodecagonal pyramids. The facets of the pits comprised typical <11-22>and <1-101> family planes.

During the growth on the pitted surface of the GaN under pitted growthconditions, there are at least two microscopic growth directions: (1)the aforementioned growth direction along the c-axis (which is anaverage growth direction), and (2) along the facets of the pits. Due tothe crystal orientation differences of these respective c-axis and facetdirection growth surfaces, the growth rate on the c-plane (c-axisgrowth) and on the facets of the pits can differ from one another andcan change differently in relation to one another with changes in thegrowth conditions.

Under conditions that promote higher growth rates in the c-axisdirection than in the facet direction of the pits, the pits will growlarger and eventually cover the growth surface. When the growthconditions that have higher growth rate on the facets of the pits thanon the c-plane are imposed, pits will be filled.

In order to maintain the pitted growth surface morphology during thegrowth, the growth rate on the c-plane should be similar to or slightlygreater than the growth rate on facets of the pits. Threadingdislocations typically follow the growth direction, and thus thedirection of the threading dislocations in the GaN film grown withpitted surface morphology will not be parallel to the c-axis, butrather, will have a tilt angle with respect to the average growthdirection.

When growing GaN for a longer period of time under pitted growthconditions, the dislocations will gradually be concentrated near thecenter of pits and at the edges of the pits. The clustering helps tobring dislocations together and dislocations with opposite Burger'svectors that meet annihilate. However, incomplete annihilation takesplace because not all the dislocations meet other dislocations.Furthermore, we have observed that dislocations concentrated near thecenter of the pits can sometimes disperse outwardly as the pits growlarger.

FIG. 8 is a DIC optical image of a GaN surface after CMP and etchingwith hot phosphoric acid. The optical image shows the concentration ofdislocations on the growth surface of the GaN material. The GaN materialwas grown under pitted growth morphology to a thickness of about 5 mm.After CMP and hot phosphoric acid etching, the dislocations weredecorated as etching pits and observed with the DIC microscope. Thedistribution of the pits was not uniform. Some areas had extremely lowdislocation density (<1E5 cm⁻²), while other areas had moderately highdislocation density (˜1E7 cm²). The dislocations concentrated in theareas that constituted the center and certain edges of the pits duringthe growth process. Under pitting growth conditions, the dislocationsdid not continue to annihilate substantially, even when the GaN materialwas grown to a thickness of 5 mm.

In accordance with the present invention, gallium nitride material isgrown to produce a large area, uniformly low dislocation density galliumnitride material, e.g., in the form of a substrate article, such as aboule or single wafer body, by first concentrating the dislocations andthen annihilating them in respective phases of the growth process.During the pitted growth phase, in which the GaN material is grown toform and develop pits in the growth surface, at least two microscopicgrowth directions exist, one along the c-axis and the other along thefacets of the pits. The growth rates on the c-plane should be similar toor slightly greater than the growth rate on facets of the pits in astable pitted growth phase, and such growth processes concentrate thedislocations near the centers and bottom portions of the pits on thegrowth surface.

After the dislocations are substantially concentrated near the bottomregions of the pits, the growth condition is changed in such manner thatthe growth rate on the facets of the pits is greater than the growthrate on the c-plane. During this second stage of the growth process, thepits will grow smaller because of the higher growth rate on the facetsof the pits. The threading dislocations in following the growthdirection are thereby concentrated and annihilate with reduction of thepit size of the pits across the growth surface, i.e., the facets of thepits will eventually grow to meet in a single point due to faster growthrate on the facets than on the c-plane, so that the concentrateddislocations meeting one another either annihilate each other or mergeinto a single dislocation.

FIGS. 9A-9E are a series of schematic illustrations showing the growthof a GaN substrate article according to one embodiment of the presentinvention, including provision of a substrate (FIG. 9A). Growth of GaNon such substrate is carried out under pitted growth conditionsproducing small pits in the GaN film on the substrate surface, withlines perpendicular to growth surface representing threadingdislocations (FIG. 9B). Note that the angle of the dislocations isexaggerated to illustrate the phenomenon. The pit-forming growth iscontinued so that the pits in the GaN material grow larger andconcentrate the dislocations in the material (FIG. 9C). Growth of theGaN material then is shifted to pit-filling growth conditions. Underthese conditions, the pits grow smaller, partially annihilating thedislocations, until pits are completely filled and all dislocations meetat the moment of pit closure, leaving a few dislocations remaining (FIG.9D). The pit-filling growth step preferably is carried out until anessentially pit-free surface is produced. The growth of the GaN materialthen is continued to form the GaN material to a desired thickness, withthe growth surface being constituted by substantially dislocation-freeGaN in such further growth, to produce a large area, uniformly lowdislocation density product GaN material (FIG. 9E).

FIGS. 10A-10B show differential interference contrast (DIC) opticalmicroscope images (FIG. 10A, top view of wafer obtained by focusing onthe surface; FIG. 10B, image underneath the surface of the same area asthe FIG. 10A view, by adjusting the focus of the microscope to theundersurface) of the defect distribution of a GaN wafer grown accordingto one embodiment of the present invention.

The dislocations were decorated as etch pits by chemical mechanicalpolishing and hot phosphoric acid etching. Due to the subtle differencebetween material grown along c-axis and the material grown along thefacets of the pits, a corresponding contrast between the two materials(c-axis material, and facet direction material) was observed under DIC.This allowed identification of the area under which growth along thefacets of the pits (pit-filling) occurred, as circled in FIG. 10. In onearea, the dislocations were completely eliminated after the pit-filling,resulting in perfect crystalline character. In other areas, only onedislocation remained after pit closure. The dislocation density for thewafer was about 1E6 cm⁻² and the defects were uniformly distributed.

The initial substrate for the growth of uniformly low dislocationdensity gallium nitride in accordance with the present invention may beof any suitable type, including, for example, gallium nitride, sapphire,silicon carbide, gallium arsenide, silicon, lithium gallate, lithiumaluminate, lithium aluminum gallate, zinc oxide, diamond, spinel,magnesium oxide, etc. It will be appreciated that different substratesmay require different substrate pretreatments prior to growth of galliumnitride in order to achieve high crystalline quality, as is readilydeterminable within the skill of the art based on the disclosure herein.

While the growth of the uniformly low dislocation density GaN wafer hasbeen described hereinabove with reference to an illustrative HVPE growthprocess, any other suitable vapor phase growth methods can be employed,such as metal-organic vapor phase epitaxy (MOVPE), metal-organicchloride method (MOC), molecular beam epitaxy (MBE), sublimation,sputtering, reactive sputtering, reactive sublimation, etc.

In addition, any combination of one or more techniques either togetheror in sequence may be considered a suitable growth technique.

The differences between various vapor phase growth methods in thisrespect resides in the manner of delivery of the growth species to thegrowth surface for forming the GaN material, and the types of the growthspecies that are employed. In MOVPE, for example, a volatileorganometallic compound of gallium such as trimethyl gallium (TMG) ortriethyl gallium (TEG) is reacted with ammonia to form gallium nitride.In sublimation, polycrystalline gallium nitride solid is sublimed toform a gallium nitride film on a substrate in a suitable ambientsublimation environment. In sputtering and reactive sputtering, a targetof gallium nitride or gallium is bombarded with ions in a suitableambient environment, such as a nitrogen or ammonia ambient, to depositGaN on the substrate. In reactive sublimation, gallium is sublimed innitrogen or ammonia, to form gallium nitride on the substrate. Theconditions for the pitted growth and for the pit-filling growth in aspecific growth method can be readily determined within the skill of artbased on the disclosure herein.

Considering the illustrative HVPE process, the growth temperature, thegrowth rate, and the NH₃:HCl ratio are controlled in the respectivephases of the two-phase process to produce the desired large area,uniformly low dislocation density GaN material. At constant temperature(1030° C., for example) and constant HCl flow (to produce constantgrowth rate, e.g., a growth rate of 150 μm/hr), increasing the NH₃ flowwill change the GaN growth process from an optimal pit-filling growthcondition that produces pit-free textured surface, to a pitted growthcondition that produces pitted surface morphology. At constant HCl andNH₃ flow (producing a constant growth rate at a constant NH₃/HCl ratio),reducing the growth temperature will change the growth condition from anoptimal pit-filling growth condition to a pitted growth condition.

The reactor geometry of the specific GaN growth reactor that is employedfor growing the GaN material of the invention will affect the flows andlocal growth environments of the growth process. It therefore isimportant to systematically investigate the growth morphology as afunction of the growth parameters, in order to identify the pittedgrowth conditions and the pit-filling growth conditions for a specificreactor employed in a given application of the present invention. Suchdetermination is readily made within the skill of the art, ashereinabove described, utilizing optical micrographs, SEM and AFMtechniques to characterize the surface in the pit-forming andpit-filling phases of the GaN growth process, to identify specificprocess conditions appropriate for forming the large area, uniformly lowdislocation density GaN material.

After identifying suitable pitted growth conditions and pit-fillinggrowth conditions, the respective growth conditions are carried outsequentially to produce uniformly low dislocation density galliumnitride as a large area, single-crystal material. The pitted growthstep, i.e., the growth of GaN under conditions serving to form pits andto concentrate dislocations at the bottoms of the pits in the material,is critical to the reduction of the overall dislocation density. Priorto the pit-filling step, the growth process is carried out so that thegrowth surface is covered with pits, so that the dislocations are sweptto the bottoms of the pits and can be annihilated in the second growthstep (pit-filling step).

In this respect, it is preferable to conduct the first step of pittedgrowth so that greater than 50% of the growth surface is covered withpits, more preferably to have greater than 75% of the surface areacovered with pits, and even more preferably to have greater than 90% ofthe growth surface covered with pits, prior to the second step ofpit-filling growth.

The reason for the preference for high coverage of the pits on thegrowth surface is that growth along the c-axis (i.e., the area notcovered with the pits) involves dislocations growing along the samedirection, so that the dislocations have substantially reduced chancefor annihilation and the final product correspondingly has higherdislocation density.

The pitted growth process, by contrast, functions to concentrate thedislocations. When the growth surface is substantially covered with thepits, the pit density is inversely proportional to the square of the pitsize. The final dislocation density after the second pit-filling stepdepends on the density of pits, since not all dislocations in the pitswill necessarily be annihilated.

Accordingly, growth of GaN to form pits over a major extent (e.g., >90%)of the GaN growth surface in the pitted growth phase, and continuingsuch growth under conditions favoring preferential growth in the facetdirection of the pits, to form larger-sized pits at the end of thepitted growth phase, prior to conducting the second phase of pit-fillinggrowth, permits the achievement of large area, uniformly low dislocationdensity GaN.

The average pit size of pits on the GaN surface prior to the pit-fillingstep preferably is greater than 25 μm, more preferably greater than 50μm, and most preferably greater than 100 μm. Such pit size is themaximum diameter or transverse dimension of the pit measured at thegrowth surface, in the plane of such surface. The upper limit of pitsize may be imposed by crystallographic factors, which at larger pitsizes increase the likelihood that polycrystalline formation within thepit will degrade rather than improve the crystalline character of thegrowing GaN material.

The position of the pits on the GaN surface can be randomly distributed,produced stochastically by the pitted growth process under thecorresponding pitted growth conditions. Alternatively, the position ofthe pits can be predetermined, by appropriate processing of the startingsubstrate.

Since the concentration of the dislocations inside the pits is due tothe facet growth direction in the pits, the nature of the facets is moreimportant than the pits themselves. Instead of patterning the startingsubstrate to produce predetermined pits, the starting substrate canalternatively be patterned to produce faceted growth morphology.

In the first step, a pitted (faceted) growth condition is used toproduce facets. The growth rate along the c-axis is faster than thegrowth rate on the facets, producing a surface covered with facets. Thedislocations are swept to the valley regions between the facets, but arenot substantially annihilated. In the second step of pit-filling, thegrowth rate on the facets is faster than the growth rate on the c-axis,so that the valleys between the facets are filled up, leading to theformation of a smooth c-axis growth material. At the moment of closureof the valleys, the dislocations are confined and they either annihilateeach other or merge into fewer dislocations. The first pitted growthphase and the second pit-filling phase may each be carried out in one ormore steps, and the vapor phase growth process may be carried out withother process steps, other than first and second phase steps, e.g.,intermediate process steps may be carried out between the first phaseand second phase steps, as may be desired in a given application of themethod of the invention.

The thickness of the pitted or faceted growth layer should be thickenough to permit substantial concentration of the dislocations near thebottom of the pits or near valleys between the facets. The thicker thepitted layer, the higher the surface coverage withdislocation-concentrating pits, thus the better the final productgallium nitride material. The pitted growth layer is preferably grown toa thickness greater than 50 μm, more preferably a thickness greater than100 μm, and even more preferably a thickness greater than 200 μm.

After growth of the pitted layer, the growth condition is changed to apit-filling condition, in which the growth rate on the facets is fasterthan the growth rate on the c-plane. The pit-filling conditionstypically involve higher growth temperature and/or lower NH₃ flow (i.e.,lower NH₃/HCl ratio) than the pitted growth condition. After the pitsare completely filled, the dislocations in the pits are substantiallyannihilated, resulting in uniformly low dislocation density GaN. Theduration of the pit-filling growth should at a minimum allow the fillingand closure of a majority of the pits, or otherwise achieve a desiredlow pit density, as appropriate to produce uniformly low dislocationdensity GaN. The duration of the pit-filling growth process necessaryfor fill of the pits is readily determinable by optical, SEM and AFMtechniques as described herein. Preferably the pit-filling growth stepis conducted until the pit density has been reduced to a level notexceeding 10 pits/cm² of the growth surface. More preferably, thepit-filling step is continued to form an essentially pit-free surface,e.g., having a pit density of 1 pit/cm² or less. Most preferably, thegrowth process is conducted in such manner as to produce a III-V nitridesingle crystal material having a totally pit-free surface.

Prior to the completion of pit-filling, two microscopic growthdirections exist, namely, the growth on the c-plane, and the growth onthe facets of the pits. After the pits are completely filled, only thec-plane growth direction exists. Considering the steps required to forma GaN wafer, which include lapping, polishing and chemical-mechanicalpolishing of the front (growth surface) as well as mechanical grindingor lapping of the back side (substrate side), the thickness of the finalc-plane growth should be such as to allow the material at the frontsurface after the GaN wafer forming steps to remain a uniformly c-planegrowth material. For such reason, in one embodiment of the invention,the thickness of the complete c-plane growth after the pits arecompletely filled is advantageously at least 50 μm. More preferably, thethickness of the GaN material is greater than 200 μm, and mostpreferably such thickness is greater than 400 μm.

The thickness of the c-plane growth may in part be determined such thatwafer fabrication yields an upper surface that is all c-plane. If thec-plane growth is not carried out for a long enough period of time afterpit closure, the surface of the finished wafer may contain recessedregions, similar to those shown in FIG. 4. If sufficient c-plane growthis carried out, a smooth, recess-free surface is produced, as shown inFIG. 3.

Additional thickness may be required to reduce impurity concentration,reduce dislocation density or to enable angle lapping for off-cut waferswith the same crystalline orientation. Longer growth (>2 mm) at thepit-filling conditions to produce a GaN ingot is advantageous, sinceunder longer growth condition, the dislocations may further annihilateand the long ingot then can be sliced into multiple wafers of largearea, uniformly low dislocation density and high quality, for subsequentdevice fabrication thereon to produce microelectronic andopto-electronic products. Alternately, multiple cycles of pit-formingand pit-filling steps can be employed to further reduce dislocationdensity. Concerning the angle of growth of the III-V nitride material inthe pits, the general growth direction in the pits should be roughlyc-axis growth but tilted.

In addition to forming large area, uniformly low dislocation density andhigh quality single crystal III-V nitride material, the process of theinvention involving pitting growth serves to substantially reduce thesusceptibility of the product III-V nitride material to cracking.

The transition from pitted growth conditions to pit-filling growthconditions can be abrupt, gradual or multi-stepped. Furthermore, eachphase of the pitted growth and pit-filling growth can involve more thanone set of growth conditions. For example, in the pitted growth phase,it may be advantageous to have a condition that produces high density ofsmaller pits at the beginning of the growth, followed by a condition togrow, coalesce and/or partly fill small pits to form larger pits at theend of the pitted growth phase. In the pit-filling phase, it may beadvantageous to have a condition that fills the pits completely,followed by a condition that produces growth on the c-plane surface at ahigher rate. Furthermore, the transition between different growthconditions may be gradual or ramped, so that the phases of pitted growthand pit-filling growth become less sharply demarcated from one another.It will also be appreciated that the growth process of the invention maybe carried out in multiple cycles of alternating pit growth andpit-filling growth steps (e.g., a first step of pit growth, followed bya second step of pit-filling growth, followed by a third step of pitgrowth, followed by a fourth step of pit-filling growth, optionally withadditional pit growth and pit-filling growth steps in sequence).

When the growth process including pitted growth and pit-filling growthis slightly deviated from the optimal condition, a few large pits maystill remain after pit-filling growth. Preferably, the density of suchgrowth pits is less than 1 cm⁻². Excluding such growth pits, the GaNmaterial has uniformly low dislocation density.

When the growth surface has pits, mechanical lap, polish and CMP canremove the pits to produce a pit-free surface. However, in this case,the surface after CMP contains a recessed area of the type shown in FIG.4. Even if the growth surface has no pits, after wafer processinginvolving lap, polish and CMP, the surface may still contain a recessedarea of the type shown in FIG. 4. The recessed area typically has higherconcentration of impurities such as oxygen or silicon. The distributionof the dislocations in the recessed area typically is not uniform.Excluding the recessed area, the surface has uniformly low dislocationdensity. Preferably, the recessed area is less than 10% of the overallwafer surface area.

It is known in the art that the impurities in a semiconductor materialaffect the electric properties of the material. For example, it iswell-established that silicon and oxygen act as shallow donors in GaN toproduce n-type conductivity. Oxygen often is un-intentionallyincorporated in GaN during HVPE growth because of gas source impuritiesand reactor leaks. Magnesium also may be introduced to the GaN materialas an impurity species that acts as an acceptor in GaN, and with properactivation, produces p-type conductivity GaN material. Additionally,transition metals may be introduced to the GaN material to function asdeep level acceptors to produce semi-insulating GaN, by compensatingresidual donor species in the GaN material.

Although un-intentionally doped HVPE GaN typically is n-type due tooxygen or silicon impurities, n-type conduction can be increased andcontrolled by intentionally introducing a silicon impurity from asilicon source such as silane or by introducing an oxygen-containinginpurity such as dioxygen in the gas stream that is fed to the GaNgrowth reactor. When impurities are present in the gas phase in thegrowth reactor, the growth conditions that produce pitted growthmorphology and pit-filling may be slightly different from those that areemployed in the absence of such impurities being introduced, and as aresult of the presence of such impurities, it may be necessary tocorrespondingly adjust the process conditions to most advantageouslycarry out doping in the pitted growth and pit filling phases of thetwo-stage process. Additionally, the amount of impurities in the growthambient and incorporation may be different during each stage of theprocess. Impurities when used can be introduced in the pitted growthstep, or in the pit-filling step, or in both the pitted growth and thepit-filling steps.

The growth of GaN on a substrate by the successive steps of pittedgrowth and pit-filling growth, in accordance with the invention,produces a GaN wafer product. Two main types of wafer-forming processescan be utilized—ingot processes and single wafer processes.

When the grown GaN material is thick, e.g., forming an ingot with alength greater than about 2 mm, a multi-wafer process is advantageouslyemployed. The ingot is oriented, ground to a pre-determined size, e.g.,≧2 inches in diameter, and sliced into multiple wafers. The ingot, as abulk GaN material article which functions as a source body forproduction of multiple wafers, typically has a thickness of at least 1mm, more preferably at least 5 mm, and most preferably at least 10 mm.After the multiple wafers are sliced from the ingot, the back and frontmain surfaces of the wafer are processed. The back side of the GaN waferis lapped and/or polished, and the front side of the GaN wafer islapped, polished and CMP-finished, to produce a GaN wafer ready forhomoepitaxial growth. The wafers may have any suitable thickness. Forexample, wafers may be formed having thicknesses in excess of 50 μm, 200μm, or 500 μm, as necessary or desired for a specific application.Ingots may also be formed with homogeneous pit growth and pit-fillinggrowth steps to produce bulk III-V nitride articles that are amenable toproducing wafers of alternative orientations, e.g., a-plane wafers,m-plane wafers, etc., as sliced from the boule and finished intopolished wafers.

When the grown GaN is not an ingot, a single-wafer process isadvantageously used to form the GaN wafer. Typically, for a single-waferprocess, the substrate for the GaN growth is not gallium nitride, andthe foreign substrate (template) is removed prior to formation of theGaN wafer. The template removal can be carried out by any suitable meansor method. For example, the template removal may involve elimination ofthe template, removal of part or all of the template, or removal of allof the template and part of the GaN adjacent to the template. Specifictechniques that may usefully be employed for such purpose includemechanical grinding, chemical etching, interfacial decomposition,interfacial fracturing, or any other means or method appropriate to theparticular template.

In a preferred embodiment, the heteroepitaxial substrate is removed insitu from the grown GaN material at a temperature in the vicinity of thegrowth temperature at the conclusion of the growth process, to yield aseparated GaN substrate article of freestanding character. Such in situremoval produces a freestanding GaN wafer substrate having no thermalcoefficient of expansion (TCE) defects therein, such as otherwise areproduced when the heteroepitaxial structure including the grown GaNmaterial and the foreign substrate are cooled to ambient (e.g., room)temperature. As an example, an in situ etching away of the foreignsubstrate at the growth temperature, or at a temperature in the vicinityof the growth temperature, e.g., within 100° C. of the growthtemperature, with a chemical etchant reagent effective for such purpose,is one approach for forming a high quality GaN substrate article in thesingle wafer process.

The grown GaN then is sized appropriately, to a predetermined size, ≧2inches diameter, for example, by an appropriate technique, such as forexample mechanical grinding, or sandblasting, or laser cutting.Subsequently, the back side of the grown GaN is lapped and/or polished,and the front side of the grown GaN is lapped, polished and CMP-finishedto produce a GaN wafer ready for homoepitaxial growth. Since the frontside of the grown GaN has higher quality than the back side of the grownGaN, the material removal from the front side is desirably minimized.Lapping and polishing of the front side is utilized mainly for thepurpose of achieving a flat wafer conformation, and lapping of thebackside is utilized primarily to achieve a desirable GaN waferthickness. The front side of the GaN wafer has uniformly low dislocationdensity. The back side may have higher dislocation density than thefront side, and the distribution of the dislocation density may be notuniform at the backside.

The chemical mechanical polish (CMP) can be carried out using anysuitable CMP formulation and CMP process. The CMP rate is slightlyhigher in the recessed area where the material was grown in thedirection along the facets of the pits on the growth surface and hashigher impurity concentration. The CMP polished surface is smooth, withsurface roughness (RMS) less than 1 nm as measured by AFM in the 10×10μm area.

During the wafer process, the wafer can be processed in such way thatthe surface of the wafer is parallel to the c-plane of the GaN crystal.Alternatively, the surface of the wafer can be at a small angle (e.g.,≦10°) with respect the crystalline c-plane. Such surface is called avicinal surface. Such vicinal GaN surface is advantageous forhomoepitaxial growth.

GaN wafers produced by the methods disclosed herein are of high qualityfor device fabrication applications, of large area, and have a lowdensity of dislocations, with the dislocations uniformly distributedacross the large area wafer surface. The density of the dislocations onthe wafer surface typically does not exceed about 1E6 cm⁻². The priorart has produced either low dislocation density but small area GaN(which is unable to be grown to larger size), or alternatively largearea GaN having non-uniformly distributed defects across the wafer. Asdiscussed herein in the Background section hereof, the prior art hasbeen unable to achieve the combination of large area single crystalgrowth of GaN and the provision of a low dislocation density that isuniformly low across the large area of the GaN substrate.

Large area, uniformly low dislocation density III-V nitride materialproduced in accordance with the present invention is formed with atleast one surface having uniformly low dislocation density. In specificembodiments, the III-V nitride material may be grown so that both mainsurfaces of the material have uniformly low dislocation density, or theIII-V nitride material may be grown so that one of such main surfaces ofthe material has uniformly low dislocation density while the other mainsurface may have high and/or non-uniform distribution of thedislocations, with dislocation density progressively decreasing from thelatter (e.g., bottom) surface to the former (e.g., top) surface.

Regardless of its specific morphological variety, the III-V nitridematerial of the invention has at least one large area surface withuniformly low dislocation density.

Large area, uniformly low dislocation density GaN wafers produced inaccordance with the present invention can be utilized as a substrate forfabrication of a wide variety of electronic and opto-electronic devicesand integrated circuitry products. The invention therefore contemplateselectronic device structures including the large area, uniformly lowdislocation density GaN wafer, on which is fabricated a device, such asfor example a laser diode, a light-emitting diode, or a high electronmobility transistor, as well as integrated circuitry including such GaNwafers, and GaN wafers of such type having at least one epitaxial layerthereon, which may be homoepitaxial or heteroepitaxial in character,depending on the specific application and end use of the GaN wafer-basedproduct.

The present invention represents a significant improvement over theprior art, in providing high-performance gallium nitride substratessuitable for fabrication of microelectronic and opto-electronic devices.

While the invention has been described herein in primary reference togallium nitride, it will be recognized that the invention is not thuslimited, but rather the aspects and advantages of the invention includeapplication of the generalized methodology hereof to the formation oflarge area, uniformly low dislocation density III-V nitride materialsother than GaN, such as for example, AlN, InN, AlInN, GaAlN, GaInN,GaAlInN, etc.

The features and advantages of the present invention are more fullyshown with respect to the following non-limiting examples.

EXAMPLE 1 Single Wafer Process

In this example, two-step GaN HVPE growth on a sapphire substrate wascarried out. In the first stage of the growth, the growth temperaturewas 1010° C., the NH₃/HCl ratio was 17, the growth rate was about 160μm/hr, and the thickness of the grown film was about 320 μm.

After the completion of the first step, the growth temperature wasraised to 1030° C., and the NH₃/HCl ratio was reduced to 8.6, and growthwas continued until the thickness of the second stage GaN material wasabout 640 μm.

After the completion of the growth, the sapphire substrate was removedfrom the thick GaN film. The GaN wafer blank was first ground about itsedge by mechanical means. The GaN wafer had two surfaces. The surfaceconstituting the growth surface was gallium-terminated. The side thatwas attached to the sapphire substrate was the nitrogen-terminated side.The gallium-side of the wafer was first lapped with coarse diamondslurry on a lap machine, and then polished with a fine diamond slurry ona polish pad. The front (gallium-side) was finished with a chemicalmechanical polish process using a mixture of colloidal silica anddiluted hydrochloric acid. The back side was lapped and polished.

FIG. 11 is a photograph of the two-sided polished gallium nitride waferproduced by the foregoing process. The diameter of the wafer was 2.3inches.

A piece of the wafer from the uniformly grown area of thegallium-terminated surface was polished by a CMP process and etched inhot phosphoric acid to determine its dislocation density. The CMPprocess and hot phosphoric acid etching decorated the dislocations asetch pits.

FIG. 12 shows a differential interference contrast (DIC) microscopeimage of the resultantly etched surface. As shown, the etch pits werevisible under the microscope. The etch pit density for the sample was5.5E5 cm⁻².

FIG. 13 shows a 100×100 μm² AFM scan of the hot phosphoric acid-etchedGaN wafer surface. The etch pit density for the image was 8.5E5 cm⁻², ingood agreement with the etch pit density counted using the DIC opticalmicroscope. Examination of the entire etched wafer under the microscopeshowed that the etch pits were uniformly distributed across the wafersurface. This example illustrates the growth of uniformly lowdislocation density, large area gallium nitride wafer, produced by themethod of the present invention.

EXAMPLE 2 GaN Ingot Process

In this example, the two-step HVPE GaN growth process was carried out togrow a relatively long GaN ingot.

In the first stage of the growth process, the growth temperature was1010° C., the NH₃/HCl ratio was 17, the growth rate was about 160 μm/hr,and the thickness of the grown film was about 320 μm.

After completion of the first step, the growth temperature was raised to1030° C., and the NH₃/HCl ratio was reduced to 12.9. Growth of the GaNmaterial was continued until the length of the ingot was 3.2 mm.

The ingot after its formation was processed into multiple wafers byslicing and subsequent lap, polish and chemical mechanical polish stepsas in Example 1. Similar two-step HVPE GaN growth processes were carriedout to grow GaN ingots having lengths on the order of 10 mm.

While the invention has been disclosed herein with reference to specificaspects, features and embodiments, it will be appreciated that theinvention is not thus limited, but rather extends to and encompassesother variations, modifications and alternative embodiments, as willsuggest themselves to those of ordinary skill in the art based on thedisclosure herein.

Accordingly, the invention is intended to be broadly construed, toencompass all such variations, modifications and alternativeembodiments, as being within the spirit and scope of the invention ashereafter claimed.

1. Large area single crystal III-V nitride material having an area of atleast 2 cm², having an average dislocation density not exceeding 3×10⁶dislocations per cm² of growth surface area, and including a pluralityof distinct regions having elevated impurity concentration, wherein eachdistinct region has at least one dimension greater than 50 microns. 2.Material according to claim 1, selected from the group consisting ofAlN, InN, GaN, AlInN, AlInGaN, InGaN, and AlGaN.
 3. GaN materialaccording to claim
 1. 4. Material according to claim 1, doped with adopant species.
 5. Material according to claim 4, of a p-doped, n-dopedor semi-insulatively doped character.
 6. Material according to claim 1,having a large area of greater than 15 cm².
 7. Material according toclaim 1, having a thickness of at least 0.1 mm.
 8. Material according toclaim 1, having an average dislocation density not exceeding 1×10⁶ cm⁻².9. Material according to claim 1, having a dislocation density standarddeviation ratio of less than 50%.
 10. Material according to claim 1,having a dislocation density standard deviation ratio of less than 25%.11. Material according to claim 1, having a large area of greater than15 cm², a thickness of at least 0.1 mm, an average dislocation densitynot exceeding 1×10⁶ cm−2, and a dislocation density standard deviationratio of less than 25%.
 12. Material according to claim 1, wherein theplurality of distinct regions having elevated impurity concentration isdisposed on an outer surface of said material.
 13. Material according toclaim 1, wherein said impurity comprises any of oxygen and silicon. 14.Material according to claim 1, wherein said plurality of distinctregions having elevated impurity concentration covers at least 50% ofthe growth surface area.
 15. Material according to claim 1, having agrowth surface with a pit density not exceeding 3 pits/cm².
 16. Materialaccording to claim 1, having a pit-free growth surface.
 17. A wafercomprising the material of claim
 1. 18. The wafer of claim 17, having adiameter of from 5 cm to 20 cm.
 19. The wafer of claim 17, having atleast one face thereof polished to a mirror finish.
 20. The wafer ofclaim 17, including a chemical mechanically polished gallium-terminatedface.
 21. The wafer of claim 17, having a surface disposed at an anglerelative to the c-plane of the III-V nitride crystal, wherein said angleis in a range of from about 0.1 to about 10 degrees.
 22. The wafer ofclaim 17, having at least one epitaxial layer thereon.
 23. An electronicdevice article, including a wafer according to claim 17 and anelectronic device structure fabricated on said wafer.
 24. The electronicdevice article of claim 23, wherein the electronic device structureincludes a laser diode.
 25. The electronic device article of claim 23,wherein the electronic device structure includes a light-emitting diode.26. The electronic device article of claim 23, wherein the electronicdevice structure includes a high electron mobility transistor.
 27. Theelectronic device article of claim 23, wherein the electronic devicestructure comprises any of an integrated circuit and an optoelectronicdevice.
 28. A wafer comprising the material of claim 1, wherein theIII-V nitride material comprises single crystal gallium nitride and thewafer includes a surface off-cut at an angle in a range of from about0.2 to about 8 degrees toward 11-20 or 10-10 from a c-plane of saidsingle crystal gallium nitride material.